2023-05-17 16:43:42 來源：鋼鐵之家閱讀量：0

牌號	304C15
對應標準	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel castings for general engineering purposes
歸類	鑄鋼
性能	耐腐蝕
標簽	奧氏體不銹鑄鋼有磁性

304C15 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni
最小值	-	-	-	-	-	18	8
最大值	0.08	1.5	2	0.04	0.04	21	11

碳當量計算

304C15 機械性能

熱處理或狀態	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷后伸長率或延伸率 δ %
ST(1000°C~1100°C)	≥480	1% proof stress Rp1.0 min ≥215	≥26

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

1 近似對照表耐蝕鑄鋼（不銹鋼鑄件）

中國

中國臺灣

日本

韓國

美國

德國

法國

俄羅斯

瑞典

英國

ISC

CNS

JIS

ASTM

UNS

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

SS₁₄

BS EN/BS

ZG07Cr19Ni9

C53048

SCS 13A

SSC 13A

CF8

J92600

GX5CrNi19-10

1.4308

Z2CN18.10M

07Х18Н9Л

2333

304C15

2 近似對照表耐蝕鑄鋼（不銹鋼鑄件）

中國		中國臺灣	日本	韓國	國際標準組織	德國		法國	俄羅斯	瑞典	英國
GB	ISC	CNS	JIS	KS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	SS₁₄	BS EN/BS
ZG07Cr19Ni9	C53048	SCS 13	SCS 13X	SSC 13	GX5CrNi19-9	GX5CrNi19-10	1.4308	Z2CN18.10M	07Х18Н9Л	2333	304C15

3 近似對照表耐蝕鑄鋼（不銹鋼鑄件）

中國	日本	美國	德國		法國	俄羅斯	英國
GB	JIS	ASTM	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG0Cr18Ni9	SUS13	CF8	G-X6CrNi18 9	1.4038	Z6CN18.10M	07Х18Н9Л	304C15

4 近似對照表耐熱鑄鋼和耐熱合金鑄件

中國	日本	美國		德國		法國	俄羅斯	英國
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG0Cr18Ni9	SCS13	CF	J92600	G-X6CrNi18 9	1.4308	Z6CN18.10M Z6CN19.9M	07Х18Н9Л	304C15

注：本資料來源于互聯網的公開資源整理，我們不保證這些資料的準確性、完整性和適用性。這些資料僅供您參考，不應用于任何商業用途或決策依據。本資料所記載的技術信息是說明產品的代表性特點和性能的參考值，對于因誤用或不當使用本資料所記載的信息等而造成的損害恕難承擔責任，敬請周知。

304C15

熱門文章